Filled silicone composition and cured silicone product

ABSTRACT

A filled silicone composition comprising (A) a curable silicone composition and (B) 5 to 60% (w/w) of a hydrophobic partially aggregated colloidal silica; and a cured silicone product comprising a reaction product of the filled silicone composition.

FIELD OF THE INVENTION

[0001] The present invention relates to a filled silicone composition and more particularly to a filled silicone composition containing a hydrophobic partially aggregated colloidal silica. The present invention also relates to a cured silicone product formed from the composition.

BACKGROUND OF THE INVENTION

[0002] Silicones are useful in a variety of applications by virtue of their unique combination of properties, including high thermal stability, good moisture resistance, excellent flexibility, high ionic purity, low alpha particle emissions, and good adhesion to various substrates. In particular, silicones containing a reinforcing filler, such as treated silica, are commonly employed in applications requiring exceptional mechanical properties. For example, filled silicones are widely used in the automotive, electronic, construction, appliance, and aerospace industries.

[0003] Silicone compositions containing hydrophobic non-aggregated colloidal silica are known in the art. For example, Kwan et al. disclose a silicone composition containing a vinyl-terminated polydimethylsiloxane, and Si—H functional crosslinker, a hydrophobic colloidal silica, and a platinum catalyst. (156^(th) ACS Rubber Division Meeting, Orlando, Fla., September 1999, paper 96).

[0004] U.S. Pat. No. 6,051,672 to Bums et al. discloses a silicone rubber composition comprising hydrophobic non-aggregated colloidal silica prepared by a method comprising reacting an aqueous suspension of a hydrophilic non-aggregated colloidal silica having an average particle diameter greater than aobut 4 nm with a silicon compound selected from the group consisting of organosilanes and organosiloxanes at a pH less than about pH 4 in the presence of a sufficient quantity of a water-miscible organic solvent to facilitate contact of the hydrophilic non-aggregated colloidal silica with the silicon compound at a temperature within a range of bout 20 C. to 25 C. for a time period sufficient to form a hydrophobic non-aggregated colloidal silica.

[0005] Although, the aforementioned silicone compositions cure to form silicone products having a wide range of mechanical properties, high concentrations, for example, 60% w/w, of hydrophobic non-aggregated colloidal silica are typically required to achieve superior mechanical properties. Consequently, there is a need for a filled silicone composition containing a low concentration of a hydrophobic colloidal silica that cures to form a silicone product having excellent mechanical properties.

SUMMARY OF THE INVENTION

[0006] The present invention is directed to a filled silicone composition comprising:

[0007] (A) a curable silicone composition; and

[0008] (B) 5 to 60% (w/w) of a hydrophobic partially aggregated colloidal silica.

[0009] The present invention is also directed to a cured silicone product comprising a reaction product of the above-described filled silicone composition.

[0010] The filled silicone composition of the present invention has numerous advantages including low VOC (volatile organic compound) content and good flow. Moreover, the filled silicone composition cures to form a cured silicone product having excellent mechanical properties, such as durometer hardness, tensile strength, elongation, modulus, and tear strength, at relatively low concentrations compared with a similar silicone composition lacking the hydrophobic partially aggregated colloidal silica. The potential advantages of low filler concentrations include shorter formulation time, lower cost, and lower viscosity.

[0011] The filled silicone composition of the present invention has numerous uses including adhesives, sealants, encapsulants, and molded articles, such as o-rings.

[0012] These and other features, aspects, and advantages of the present invention will become better understood with reference to the following description and appended claims.

DETAILED DESCRIPTION OF THE INVENTION

[0013] A filled silicone composition according to the present invention comprises:

[0014] (A) a curable silicone composition; and

[0015] (B) 5 to 60% (w/w) of a hydrophobic partially aggregated colloidal silica.

[0016] Component (A) is a curable silicone composition. Curable silicone compositions and methods for their preparation are well known in the art. Examples of curable silicone compositions include, but are not limited to, hydrosilylation-curable silicone compositions, peroxide curable silicone compositions, condensation-curable silicone compositions, epoxy-curable silicone compositions; ultraviolet radiation-curable silicone compositions, and high-energy radiation-curable silicone compositions. For example, a suitable hydrosilylation-curable silicone composition typically comprises (i) an organopolysiloxane containing an average of at least two silicon-bonded alkenyl groups per molecule, (ii) an organohydrogensiloxane containing an average of at least two silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure the composition, and (iii) a hydrosilylation catalyst. The hydrosilylation catalyst can be any of the well known hydrosilylation catalysts comprising a platinum group metal, a compound containing a platinum group metal, or a microencapsulated platinum group metal-containing catalyst. Platinum group metals include platinum, rhodium, ruthenium, palladium, osmium and iridium. Preferably, the platinum group metal is platinum, based on its high activity in hydrosilylation reactions.

[0017] The hydrosilylation-curable silicone composition can be a one-part composition or a multi-part composition comprising the components in two or more parts. Room-temperature vulcanizable (RTV) compositions typically comprise two parts, one part containing the organopolysiloxane and catalyst and another part containing the organohydrogensiloxane and any optional ingredients. Hydrosilylation-curable silicone compositions that cure at elevated temperatures can be formulated as one-part or multi-part compositions. For example, liquid silicone rubber (LSR) compositions are typically formulated as two-part systems. One-part compositions typically contain a platinum catalyst inhibitor to ensure adequate shelf life.

[0018] A suitable peroxide-curable silicone composition typically comprises (i) an organopolysiloxane and (ii) an organic peroxide. Examples of organic peroxides include, diaroyl peroxides such as dibenzoyl peroxide, di-p-chlorobenzoyl peroxide, and bis-2,4-dichlorobenzoyl peroxide; dialkyl peroxides such as di-t-butyl peroxide and 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane; diaralkyl peroxides such as dicumyl peroxide; alkyl aralkyl peroxides such as t-butyl cumyl peroxide and 1,4-bis(t-butylperoxyisopropyl)benzene; and alkyl aroyl peroxides such as t-butyl perbenzoate, t-butyl peracetate, and t-butyl peroctoate.

[0019] A condensation-curable silicone composition typically comprises (i) an organopolysiloxane containing an average of at least two hydroxy groups per molecule; and (ii) a tri- or tetra-functional silane containing hydrolysable Si—O or Si—N bonds. Examples of silanes include alkoxysilanes such as CH₃Si(OCH₃)₃, CH₃Si(OCH₂CH₃)₃, CH₃Si(OCH₂CH₂CH₃)₃, CH₃Si[O(CH₂)₃CH₃]₃, CH₃CH₂Si(OCH₂CH₃)₃, C₆H₅Si(OCH₃)₃, C₆H₅CH₂Si(OCH₃)₃, C₆H₅Si(OCH₂CH₃)₃, CH₂═CHSi(OCH₃)₃, CH₂═CHCH₂Si(OCH₃)₃, CF₃CH₂CH₂Si(OCH₃)₃, CH₃Si(OCH₂CH₂OCH₃)₃, CF₃CH₂CH₂Si(OCH₂CH₂OCH₃)₃, CH₂═CHSi(OCH₂CH₂OCH₃)₃, CH₂═CHCH₂Si(OCH₂CH₂OCH₃)₃, C₆H₅Si(OCH₂CH₂OCH₃)₃, Si(OCH₃)₄, Si(OC₂H₅)₄, and Si(OC₃H₇)₄; organoacetoxysilanes such as CH₃Si(OCOCH₃)₃, CH₃CH₂Si(OCOCH₃)₃, and CH₂═CHSi(OCOCH₃)₃; organoiminooxysilanes such as CH₃Si[O—N═C(CH₃)CH₂CH₃]₃, Si[O—N═C(CH₃)CH₂CH₃]₄, and CH₂═CHSi[O—N═C(CH₃)CH₂CH₃]₃; organoacetamidosilanes such as CH₃Si[NHC(═O)CH₃]₃ and C₆H₅Si[NHC(═O)CH₃]₃; aminosilanes such as CH₃Si[NH(s-C₄H₉)]₃ and CH₃Si(NHC₆H₁₁)₃; and organoaminooxysilanes.

[0020] A condensation-curable silicone composition can also contain a condensation catalyst to initiate and accelerate the condensation reaction. Examples of condensation catalysts include, but are not limited to, amines; and complexes of lead, tin, zinc, and iron with carboxylic acids. Tin(II) octoates, laurates, and oleates, as well as the salts of dibutyl tin, are particularly useful. The condensation-curable silicone composition can be a one-part composition or a multi-part composition comprising the components in two or more parts. For example, room-temperature vulcanizable (RTV) compositions can be formulated as one-part or two-part compositions. In the two-part composition, one of the parts typically includes a small amount of water.

[0021] A suitable epoxy-curable silicone composition typically comprises (i) an organopolysiloxane containing an average of at least two epoxy-functional groups per molecule and (ii) a curing agent. Examples of epoxy-functional groups include 2-glycidoxyethyl, 3-glycidoxypropyl, 4-glycidoxybutyl, 2,(3,4-epoxycyclohexyl)ethyl, 3-(3,4-epoxycyclohexyl)propyl, 2,3-epoxypropyl, 3,4-epoxybutyl, and 4,5-epoxypentyl. Examples of curing agents include anhydrides such as phthalic anhydride, hexahydrophthalic anhydride, tetrahydrophthalic anhydride, and dodecenylsuccinic anhydride; polyamines such as diethylenetriamine, triethylenetetramine, diethylenepropylamine, N-(2-hydroxyethyl)diethylenetriamine, N,N′-di(2-hydroxyethyl)diethylenetriamine, m-phenylenediamine, methylenedianiline, aminoethyl piperazine, 4,4-diaminodiphenyl sulfone, benzyldimethylamine, dicyandiamide, and 2-methylimidazole, and triethylamine; Lewis acids such as boron trifluoride monoethylamine; polycarboxylic acids; polymercaptans; polyamides; and amidoamines.

[0022] A suitable ultraviolet radiation-curable silicone composition typically comprises (i) an organopolysiloxane containing radiation-sensitive functional groups and (ii) a photoinitiator. Examples of radiation-sensitive functional groups include acryloyl, methacryloyl, mercapto, epoxy, and alkenyl ether groups. The type of photoinitiator depends on the nature of the radiation-sensitive groups in the organopolysiloxane. Examples of photoinitiators include diaryliodonium salts, sulfonium salts, acetophenone, benzophenone, and benzoin and its derivatives.

[0023] A suitable high-energy radiation-curable silicone composition comprises an organopolysiloxane polymer. Examples of organpolyosiloxane polymers include polydimethylsiloxanes, poly(methylvinylsiloxanes), and organohydrogenpolysiloxanes. Examples of high-energy radiation include y-rays and electron beams.

[0024] Component (B) is at least one hydrophobic partially aggregated colloidal silica. As used herein, the term “hydrophobic partially aggregated colloidal silica” refers to the product prepared by a method comprising reacting (1) a silica sol comprising at least one hydrophilic partially aggregated colloidal silica with (2) an organosilicon compound selected from (a) at least one organosilane having the formula R¹ _(a)H_(b)SiX_(4-a-b), (b) at least one organocyclosiloxane having the formula (R¹ ₂SiO)_(m), (c) at least one organosiloxane having the formula R¹ ₃SiO(R¹SiO)_(n)SiR¹ ₃, and (d) a mixture comprising at least two of (a) (b), and (c), in the presence of (3) water (4) an effective amount of a water-miscible organic solvent, and (5) an acid catalyst, to produce the hydrophobic partially aggregated colloidal silica and an aqueous phase, wherein R¹ is hydrocarbyl or substituted hydrocarbyl; X is a hydrolysable group; a is 0, 1, 2, or 3; b is 0 or 1 ; a+b=1, 2, or 3, provided when b=1, a+b=2 or 3; m has an average value of from 3 to 10; and n has an average value of from 0 to 10.

[0025] Component (1) is a silica sol comprising at least one hydrophilic partially aggregated colloidal silica. As used herein, the term “silica sol” refers to a stable suspension of hydrophilic partially aggregated colloidal silica particles in water, an organic solvent, or a mixture of water and a water-miscible organic solvent. Also, as used herein, the term “hydrophilic” means the silica surface has silanol (Si—OH) groups capable of hydrogen bonding with suitable donors, such as adjacent silanol groups and water molecules. In other words, the silanol groups produced during manufacture of the silica have not been modified, for example, by reaction with an organic or organosilicon compound. Further, as used herein, the term “partially aggregated colloidal silica” refers to colloidal silica comprising particles having a ratio D₁/D₂ of at least 3, where D₁ is the mean diameter of the colloidal silica particles measured by a dynamic light-scattering method and D₂ is the mean diameter of the colloidal silica particles as determined by a nitrogen adsorption method, and D₁ has a value of from 40 to 500 nm. The value of D₁ can be determined using a conventional light-scattering apparatus according to the well known method described in J. Chem. Phys. 1972, 57 (11), 4814. The value of D₂ can be calculated according to the equation D₂=2720/S, where S is the specific surface area of the colloidal silica as determined by nitrogen absorption according to the Brunauer-Emmett-Teller (BET) method. Additionally, aqueous silica sols typically have a pH of from 7 to 11.

[0026] Examples of silica sols suitable for use as component (1) include, but are not limited to, a moniliform silica sol disclosed by Watanabe et al. in European Patent Application No. EP 1114794 A1 and an elongated-shaped silica sol disclosed by Watanabe et al. in U.S. Pat. No. 5,597,512. The moniliform (rosary- or pearl necklace-shaped) silica sol has an SiO₂ concentration of 1 to 50% (w/w) and contains liquid medium-dispersed moniliform colloidal silica particles having a ratio D₁/D₂ of at least 3, wherein the moniliform colloidal silica particles comprise spherical colloidal silica particles having a mean diameter of 10 to 80 nm and metal oxide-containing silica bonding the spherical colloidal silica particles, wherein the spherical colloidal silica particles are linked in rows in only one plane; and D₁ and D₂ are as defined above, wherein D₁ has a value of from 50 to 500 nm. The length of the moniliform colloidal silica particles is typically at least five times the mean diameter of the spherical colloidal silica particles, as determined by electron micrographs. The silica bonding the spherical colloidal silica particles contains a small amount, 0.5 to 10% (w/w), of a divalent or trivalent metal oxide, based on the weight of SiO₂ in the silica bonding the spherical colloidal silica particles, depending on the method of preparing the moniliform silica sol.

[0027] The moniliform silica sol typically contains not greater than 50% (w/w), preferably 5 to 40% (w/w), of SiO₂. The viscosity of the silica sol is typically from several mPa-s to about 1,000 mPa.s at room temperature.

[0028] Examples of moniliform silica sol include the aqueous suspensions of colloidal silica sold by Nissan Chemical Industries, Ltd. (Tokyo, Japan) under the trade names SNOWTEX-PS-S and SNOWTEX-PS-M, described in the Examples section below.

[0029] The moniliform silica sol can be prepared as described in detail by Watanabe et al. in European Patent Application No. EP 1114794 A1. Briefly stated, the method comprises: (a) adding an aqueous solution containing a water-soluble divalent metal salt or a water-soluble trivalent metal salt singly or in admixture to an active silicic acid-containing aqueous colloidal liquid or an acidic silica sol having a mean particle diameter of 3 to 8 nm, each containing 0.5 to 10% (w/w) of SiO₂ and having a pH of 2 to 6, in an amount of 1 to 10% (w/w) as a metal oxide based on SiO₂ in the aqueous colloidal solution of active silicic acid or acidic silica sol and mixing them; (b) adding acidic spherical silica sol having a mean diameter of 10 to 80 nm and a pH 2 to 6 to the mixed liquid (a) obtained in step (a) in such an amount that a ratio of a silica content (A) derived from the acidic spherical silica sol to a silica content (B) derived from the mixed liquid (b), A/B (weight ratio), is 5 to 100 and the total silica content (A+B) of a mixed liquid (b) obtained by mixing the acidic spherical silica sol with the mixed liquid (a) has an SiO₂ concentration of 5 to 40% (w/w) in the mixed liquid (b) and mixing them; (c) adding an alkali metal hydroxide, water-soluble organic base or water-soluble silicate to the mixed liquid (b) obtained in step (b) such that the pH is 7 to 11 and mixing them; and (d) heating the mixed liquid (c) obtained in step (c) at 100 to 200° C. for 0.5 to 50 h.

[0030] The elongated-shaped silica sol has an SiO₂ concentration of 6 to 30% (w/w) and contains elongated-shaped amorphous colloidal silica particles having a ratio D₁/D₂ of at least 5, wherein D₁ and D₂ are as defined above for the moniliform colloidal silica particles and D₁ has a value of from 40 to 300 nm; and the particles are elongated in only one plane and have a uniform thickness along the elongation within the range of from 5 to 20 nm, as determined using an electron microscope. The colloidal silica particles are substantially amorphous silica, but they may contain a small amount, typically 1500 to 8500 ppm, of an oxide of calcium or magnesium, or both, based on the weight of SiO₂ in the silica sol. In some cases, the silica particles may contain a slight amount of oxides of other polyvalent metals in addition to the oxides of calcium and/or magnesium. The total concentration of metal oxides is typically from 1500 to 15000 ppm, based on the weight of SiO₂ in the silica sol. Examples of polyvalent metals include strontium, barium, zinc, tin, lead, copper, iron, nickel cobalt, manganese, aluminum, chromium, yttrium, and titanium.

[0031] The elongated-shaped silica sol can be prepared as described in detail by Watanabe et al. in U.S. Pat. No. 5,597,512. Briefly stated, the method comprises: (a) mixing an aqueous solution containing a water-soluble calcium salt or magnesium salt or a mixture of said calcium salt and said magnesium salt with an aqueous colloidal liquid of an active silicic acid containing from 1 to 6% (w/w) of SiO₂ and having a pH in the range of from 2 to 5 in an amount of 1500 to 8500 ppm as a weight ratio of CaO or MgO or a mixture of CaO and MgO to SiO₂ of the active silicic acid; (b) mixing an alkali metal hydroxide or a water-soluble organic base or a water-soluble silicate of said alkali metal hydroxide or said water-soluble organic base with the aqueous solution obtained in step (a) in a molar ratio of SiO₂/M₂O of from 20 to 200, where SiO₂ represents the total silica content derived from the active silicic acid and the silica content of the silicate and M represents an alkali metal atom or organic base molecule; and (c) heating at least a part of the mixture obtained in step (b) to 60° C. or higher to obtain a heel solution, and preparing a feed solution by using another part of the mixture obtained in step (b) or a mixture prepared separately in accordance with step (b), and adding said feed solution to said heel solution while vaporizing water from the mixture during the adding step until the concentration of SiO₂ is from 6 to 30% (w/w). The silica sol produced in step (c) typically has a pH of from 8.5 to 11.

[0032] Component (1) can be a silica sol comprising a single hydrophilic partially aggregated colloidal silica as described above or a silica sol comprising two or more such colloidal silicas that differ in at least one property, such as surface area, pore diameter, pore volume, particle size, and particle shape.

[0033] Component (2) is at least one organosilicon compound selected from (2)(a), (2)(b), (2)(c), and (2)(d), each described below.

[0034] Component (2)(a) is at least one organosilane having the formula R¹ _(a)H_(b)SiX_(4-a-b), wherein R¹ is hydrocarbyl or substituted hydrocarbyl; X is a hydrolysable group; a is 0, 1, 2, or 3; b is 0 or 1; and a+b=1, 2, or 3, provided when b=1, a+b=2 or 3. The hydrocarbyl groups and substituted hydrocarbyl groups represented by R¹ typically have from 1 to 20 carbon atoms, alternatively from 1 to 10 carbon atoms, alternatively from 1 to 6 carbon atoms. Acyclic hydrocarbyl and substituted hydrocarbyl groups containing at least 3 carbon atoms can have a branched or unbranched structure.

[0035] Examples of hydrocarbyl groups include, but are not limited to, alkyl, such as methyl, ethyl, propyl, 1-methylethyl, butyl, 1-methylpropyl, 2-methylpropyl, 1,1-dimethylethyl, pentyl, 1-methylbutyl, 1-ethylpropyl, 2-methylbutyl, 3-methylbutyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, and octadecyl; cycloalkyl, such as cyclopentyl, cyclohexyl, and methylcyclohexyl; aryl, such as phenyl and naphthyl; alkaryl, such as tolyl and xylyl; aralkyl, such as benzyl and phenethyl; alkenyl, such as vinyl, allyl, and propenyl; arylalkenyl, such as styryl and cinnamyl; and alkynyl, such as ethynyl and propynyl.

[0036] Examples of substitutents include —OH, —NH₂, —SH, —CO₂H, —O(O═C)CR², —(R²)N(O═)CR², and —S—S—R², wherein R² is C₁ to C₈ hydrocarbyl.

[0037] As used herein, the term “hydrolysable group” The term “hydrolysable group” means the Si—X group can react with water to form an Si—OH group. Examples of hydrolysable groups include, but are not limited to, —Cl, Br, —OR³, —OCH₂CH₂OR³, CH₃C(═O)O—, Et(Me)C═N—O—, CH₃C(═O)N(CH₃)—, and —ONH₂, wherein R³ is C₁ to C₈ hydrocarbyl or halogen-substituted hydrocarbyl.

[0038] Examples of hydrocarbyl groups represented by R³ include, but are not limited to, unbranched and branched alkyl, such as methyl, ethyl, propyl, 1-methylethyl, butyl, 1-methylpropyl, 2-methylpropyl, 1,1-dimethylethyl, pentyl, 1-methylbutyl, 1-ethylpropyl, 2-methylbutyl, 3-methylbutyl, 1,2-dimethylpropyl, 2,2-dimethylpropyl, hexyl, heptyl, and octyl; cycloalkyl, such as cyclopentyl, cyclohexyl, and methylcyclohexyl; phenyl; alkaryl, such as tolyl and xylyl; aralkyl, such as benzyl and phenethyl; alkenyl, such as vinyl, allyl, and propenyl; arylalkenyl, such as styryl; and alkynyl, such as ethynyl and propynyl. Examples of halogen-substituted hydrocarbyl groups include, but are not limited to, 3,3,3-trifluoropropyl, 3-chloropropyl, chlorophenyl, and dichlorophenyl.

[0039] Examples of organosilanes include, but are not limited to, SiCl₄, CH₃SiCl₃, CH₃CH₂SiCl₃, C₆H₅SiCl₃, (CH₃)₂SiCl₂, (CH₃CH₂)₂SiCl₂, (C₆H₅)₂SiCl₂, (CH₃)₃SiCl, CH₃HSiCl₂, (CH₃)₂HSiCl, SiBr₄, CH₃SiBr₃, CH₃CH₂SiBr₃, C₆H₅SiBr₃, (CH₃)₂SiBr₂, (CH₃CH₂)₂SiBr₂, (C₆H₅)₂SiBr₂(CH₃)₃SiBr, CH₃HSiBr₂, (CH₃)₂HSiBr, Si(OCH₃)₄, CH₃Si(OCH₃)₃, CH₃Si(OCH₂CH₃)₃, CH₃Si(OCH₂CH₂CH₃)₃, CH₃Si[O(CH₂)₃CH₃]₃, CH₃CH₂Si(OCH₂CH₃)₃, C₆H₅Si(OCH₃)₃, C₆H₅CH₂Si(OCH₃)₃, C₆H₅Si(OCH₂CH₃)₃ CH₂═CHSi(OCH₃)₃, CH₂═CHCH₂Si(OCH₃)₃, CF₃CH₂CH₂Si(OCH₃)₃)₃, (CH₃)₂Si(OCH₃)₂, (CH₃)₂Si(OCH₂CH₃)₂, (CH₃)₂Si(OCH₂CH₂CH₃)₂, (CH₃)₂Si[O(CH₂)₃CH₃]₂, (CH₃CH₂)₂Si(OCH₂CH₃)₂, (C₆H₅)₂Si(OCH₃)₂, (C₆H₅CH₂)₂Si(OCH₃)₂, (C₆H₅)₂Si(OCH₂CH₃)₂, (CH₂═CH)₂Si(OCH₃)₂, (CH₂═CHCH₂)₂Si(OCH₃)₂, (CF₃CH₂CH₂)₂Si(OCH₃)₂, (CH₃)₃SiOCH₃, CH₃HSi(OCH₃)₂, (CH₃)₂HSiOCH₃, CH₃Si(OCH₂CH₂OCH₃)₃, CF₃CH₂CH₂Si(OCH₂CH₂OCH₃)₃, CH₂═CHSi(OCH₂CH₂OCH₃)₃, CH₂═CHCH₂Si(OCH₂CH₂OCH₃)₃, and C₆H₅Si(OCH₂CH₂OCH₃)₃, (CH₃)₂Si(OCH₂CH₂OCH₃)₂, (CF₃CH₂CH₂)₂Si(OCH₂CH₂OCH₃)₂, (CH₂═CH)₂Si(OCH₂CH₂OCH₃)₂, (CH₂═CHCH₂)₂Si(OCH₂CH₂OCH₃)₂, (C₆H₅)₂Si(OCH₂CH₂OCH₃)₂, CH₃Si(OAc)₃, CH₃CH₂Si(OAc)₃, CH₂═CHSi(OAc)₃, (CH₃)₂Si(OAc)₂, (CH₃CH₂)₂Si(OAc)₂, (CH₂═CH)₂Si(OAc)₂, CH₃Si[ON═C(CH₃)CH₂CH₃]₃, (CH₃)₂Si[ON═C(CH₃)CH₂CH₃]₂, CH₃Si[NHC(═O)CH₃]₃, C₆H₅Si[NHC(═O)CH₃]₃, (CH₃)₂Si[NHC(═O)CH₃]₂, and Ph₂Si[NHC(═O)CH₃]₂, wherein OAc is CH₃C(═O)O— and Ph is phenyl.

[0040] Component (2)(a) can be a single organosilane or a mixture comprising two or more different organosilanes, each having the formula R¹ _(a)H_(b)SiX_(4-a-b), wherein R¹, X, a, and b are as defined above. Methods of preparing organosilanes suitable for use as component (2)(a) are well known in the art; many of these organosilanes are commercially available.

[0041] Component (2)(b) is at least one organocyclosiloxane having the formula (R¹ ₂SiO)_(m), wherein R¹ is as defined and exemplified above for component (2)(a) and m has an average value of from 3 to 10, alternatively from 3 to 8, alternatively from 3 to 5.

[0042] Examples of organocylclosiloxanes include, but are not limited to, hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, and decamethylcyclopentasiloxane.

[0043] Component (2)(b) can be a single organocylcosiloxane or a mixture comprising two or more different organocyclosiloxanes that differ in at least one property, such as structure, viscosity, average molecular weight, siloxane units, and sequence. Methods of preparing organocyclosiloxanes suitable for use as component (2)(b) are well known in the art; many of these organocyclosiloxanes are commercially available.

[0044] Component (2)(c) is at least one organosiloxane having the formula R¹ ₃SiO(R¹SiO)_(n)SiR¹ ₃, wherein R¹ is as defined and exemplified above for component (2)(a) and n has an average value of from 0 to 10, alternatively from 0 to 8, alternatively from 0 to 4.

[0045] Examples of organosiloxanes include, but are not limited to, hexamethyldisiloxane, hexaethyldisiloxane, 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, octamethyltrisiloxane, and decamethyltetrasiloxane.

[0046] Component (2)(c) can be a single organosiloxane or a mixture comprising two or more different organosiloxanes that differ in at least one property, such as structure, viscosity, average molecular weight, siloxane units, and sequence. Methods of preparing organosiloxanes suitable for use as component (2)(c) are well known in the art; many of these organosiloxanes are commercially available.

[0047] Component (2) can be a single organosilicon compound represented by components (2)(a), (2)(b), and (2)(c), or a mixture comprising at least two of the components.

[0048] Component (4) is at least one water-miscible organic solvent. As used herein, the term “water-miscible” means the organic solvent is substantially miscible with water or completely miscible (i.e., miscible in all proportions) with water. For example, the solubility of the water-miscible organic solvent in water is typically at least 90 g/100 g of water at 25° C.

[0049] Examples of water-miscible organic solvents include, but are not limited to, monohydric alcohols such as methanol, ethanol, 1-propanol, and 2-propanol; dihydric alcohols such as ethylene glycol and propylene glycol; polyhydric alcohols such as glycerol and pentaerythritiol; and dipolar aproptic solvents such as N,N-dimethylformamide, tetrahydrofuran, dimethylsulfoxide, and acetonitrile. Component (4) can be a single water-miscible organic solvent or a mixture comprising two or more different water-miscible organic solvents, each as defined above.

[0050] Component (5) is at least one acid catalyst that promotes reaction of the hydrophilic partially aggregated colloidal silica with the organosilicon compound, component (2). Although the acid catalyst is typically added as a separate component to the reaction mixture, in some cases it can be produced in situ. For example, when component (2) is an organosilane containing a hydrolysable group such as chloro, a portion or all of the acid catalyst may be generated by reaction of the chlorosilane with water or the hydroxy groups of the hydrophilic partially aggregated colloidal silica.

[0051] Examples of acid catalysts include inorganic acids such as hydrochloric acid, sulfuric acid, nitric acid, and hydrofluoric acid; and organic acids such as acetic acid, oxalic acid, and trifluoroacetic acid. The acid can be a single acid or a mixture comprising two or more different acids.

[0052] The method of the present invention can be carried out in any standard reactor suitable for contacting silica with an organosilicon compound in the presence of water and an acid catalyst. Suitable reactors include glass and Teflon-lined glass reactors. Preferably, the reactor is equipped with an efficient means of agitation, such as a stirrer.

[0053] The silica sol, component (1), is typically added to a mixture comprising the organosilicon compound, water, the water-miscible organic solvent, and the acid catalyst. Reverse addition, i.e., addition of a mixture comprising the organosilicon compound to the silica sol is also possible. However, reverse addition may result in formation of larger aggregates of the colloidal silica.

[0054] The rate of addition of the silica sol to the mixture containing the organosilicon compound is typically from 1 to 3 mL/min for a 0.5-L reaction vessel equipped with and efficient means of stirring. When the rate of addition is too slow, the reaction time is unnecessarily prolonged. When the rate of addition is too fast, the colloidal silica may form larger aggregates.

[0055] The suspension of the hydrophilic partially aggregated colloidal silica and the organosilicon compound are typically reacted at a temperature of from 20 to 150° C., alternatively from 40 to 120° C., alternatively from 60 to 100° C. When the temperature is less than 40° C., the rate of reaction is typically very slow.

[0056] The reaction is carried out for a period of time sufficient to produce the hydrophobic partially aggregated colloidal silica, and an aqueous phase. The reaction time depends on a number of factors including the nature of the hydrolysable groups in the organosilicon compound, structure of the organosilicon compound, agitation of the reaction mixture, concentration of the hydrophilic partially aggregated colloidal silica, and temperature. The reaction time is typically from several minutes to several hours. For example, the reaction time is typically from 0.1 to 2 h at a temperature of from 40 to 120° C., alternatively from 0.5 to 1 h at a temperature of from 60 to 100° C. The optimum reaction time can be determined by routine experimentation using the methods set forth in the Examples below.

[0057] The concentration of the hydrophilic partially aggregated colloidal silica of component (1) in the reaction mixture is typically from 1 to 20% (w/w), alternatively from 1 to 10% (w/w), alternatively from 1 to 5% (w/w), based on the total weight of the reaction mixture.

[0058] The mole ratio of the organosilicon compound, component (2), to the hydrophilic partially aggregated colloidal silica (SiO₂) of component (1) is typically from 0.1 to 5, alternatively from 0.2 to 3, alternatively from 0.5 to 2. When the mole ratio of component (2) to the hydrophilic partially aggregated colloidal silica is less than 0. 1, the treated silica may not exhibit hydrophobic properties. When the mole ratio is greater than 5, the hydrophobic colloidal silica may not precipitate from the aqueous phase, as described below.

[0059] The concentration of water, component (3), in the reaction mixture is typically from 20 to 60% (w/w), alternatively from 20 to 50% (w/w), alternatively from 20 to 40% (w/w), based on the total weight of the reaction mixture. When component (1) is an aqueous silica sol, a portion or all of component (3) may be supplied by the silica sol.

[0060] The water-miscible organic solvent, component (4), is present in an effective amount in the reaction mixture. As used herein, the term “effective amount” means the concentration of component (4) is such that the organosilicon compound is soluble in the aqueous reaction mixture containing the water-miscible organic solvent, and the partially aggregated colloidal silica particles in the reaction mixture are stable, i.e., the particles do not form larger aggregates. Aggregation of the hydrophilic partially aggregated colloidal silica particles can be detected by comparing the size and shape of the hydrophobic colloidal silica particles with the size and shape of the hydrophilic partially aggregated colloidal silica particles of component (1) using electron microscopy. The concentration of component (4) is typically from about 5 to about 35% (v/v), alternatively from 10 to 30% (v/v), alternatively from 20 to 30% (v/v), based on the total volume of the reaction mixture. When the concentration of component (4) is less than 5% (v/v), the treated silica may not exhibit hydrophobic properties. When the concentration of component (4) is greater than 35% (v/v), the hydrophobic colloidal silica may not precipitate from the aqueous phase, as described below. The effective amount of component (4) can be determined by routine experimentation using the methods in the Examples below.

[0061] The concentration of component (5) is sufficient to maintain the pH of the reaction mixture at a value less than 4. For example, the concentration of component (5) is typically from 10 to 60% (w/w), alternatively from 10 to 40% (w/w), based on the total weight of the reaction mixture. When the concentration of component (5) is less than 10% (w/w), the rate of reaction may be too slow for commercial applications. When the concentration of component (5) is greater than 60% (w/w), additional washing steps may be required to remove the acid from the hydrophobic partially aggregated colloidal silica.

[0062] The hydrophobic partially aggregated colloidal silica typically precipitates from the aqueous phase. As used herein, the term “precipitates” means the hydrophobic partially aggregated colloidal silica forms a deposit that is insoluble in the aqueous phase. For example, the hydrophobic colloidal silica may float to the top of the aqueous phase, settle to the bottom of the aqueous phase, or collect on the walls of the reaction vessel. The hydrophobic silica is typically separated from the aqueous phase by removing (for example, draining or decanting) the aqueous phase or the hydrophobic silica.

[0063] The hydrophobic silica, isolated as described above, is typically washed with water to remove residual acid. The water can further comprise a water-miscible organic solvent, such as 2-propanol. The concentration of the water-miscible organic solvent in the aqueous wash is typically from 10 to 30% (v/v). The hydrophobic silica can be washed by mixing it with water and then separating the hydrophobic silica from the water. The organic phase is typically washed from one to three times with separate portions of water. The volume of water per wash is typically from two to five times the volume of the hydrophobic partially aggregated colloidal silica.

[0064] The washed hydrophobic silica is typically dried by suspending it in a water-immiscible organic solvent and then removing the organic solvent using a process such as evaporating or spray drying. As used herein, the term “water-immiscible” means the organic solvent is slightly miscible or completely immiscible with water. For example, the solubility of water in the solvent is typically less than about 0.1 g/100 g of solvent at 25° C. The organic solvent can be any aprotic or dipolar aprotic organic solvent that is immiscible with water. Preferably, the organic solvent forms a minimum boiling azeotrope with water. If the organic solvent does not form an azeotrope with water, the organic solvent preferably has a boiling point greater than the boiling point of water.

[0065] Examples of water-immiscible organic solvents include, but are not limited to, saturated aliphatic hydrocarbons such as n-pentane, hexane, n-heptane, isooctane and dodecane; cycloaliphatic hydrocarbons such as cyclopentane and cyclohexane; aromatic hydrocarbons such as benzene, toluene, xylene and mesitylene; cyclic ethers such as tetrahydrofuran (THF) and dioxane; ketones such as methyl isobutyl ketone (MIBK); halogenated alkanes such as trichloroethane; and halogenated aromatic hydrocarbons such as bromobenzene and chlorobenzene. The water-immiscible organic solvent can be a single organic solvent or a mixture comprising two or more different organic solvents, each as defined above.

[0066] Additionally, before removing the water-immiscible organic solvent, as described above, the suspension of the hydrophobic silica in the organic solvent can be distilled to remove water. The distillation can be carried out at atmospheric or subatmospheric pressure at a temperature that depends on the boiling point of the water-immiscible organic solvent. The distillation is typically continued until the distillate is free of water.

[0067] Under certain conditions, the hydrophobic partially aggregated colloidal silica remains suspended in the aqueous phase of the reaction mixture. In this case, the aqueous suspension of the hydrophobic silica is typically treated with a water-immiscible organic solvent in an amount sufficient to form a non-aqueous phase comprising the water-immiscible organic solvent and the hydrophobic silica. Suitable water-immiscible organic solvents are described above. The concentration of the water-immiscible organic solvent is typically from 5 to 20% (v/v), alternatively from 10 to 20% (v/v), based on the total volume of the aqueous suspension.

[0068] The non-aqueous phase is typically separated from the aqueous phase by discontinuing agitation of the mixture, allowing the mixture to separate into two layers, and removing the aqueous or non-aqueous layer.

[0069] The non-aqueous phase, isolated as described above, is typically washed with water to remove residual acid. The water can further comprise a water-miscible organic solvent, such as 2-propanol. The concentration of the water-miscible organic solvent in the solution is typically from 10 to 30% (v/v). The non-aqueous phase can be washed by mixing it with water, allowing the mixture to separate into two layers, and removing the aqueous layer. The organic phase is typically washed from one to three times with separate portions of water. The volume of water per wash is typically from two to five times the volume of the non-aqueous phase.

[0070] The hydrophobic silica is typically dried by removing the water-immiscible organic solvent using a method such as evaporating or spray-drying.

[0071] Additionally, before removing the water-immiscible organic solvent, the non-aqueous phase can be distilled to remove water. The distillation can be carried out at atmospheric or subatmospheric pressure at a temperature that depends on the boiling point of the water-immiscible organic solvent. The distillation is typically continued until the distillate is free of water. The distillation is typically continued until the distillate is free of water.

[0072] The hydrophobic partially aggregated colloidal silica prepared by the method of the present invention typically has a surface area of from 20 to 300 m²/g, alternatively from 50 to 200 m²/g, alternatively from 50 to 150 m²/g, as determined by nitrogen adsorption according to the BET method. Also, the hydrophobic colloidal silica typically has a pore diameter of from 50 to 300 Å, alternatively from 100 to 250 Å, alternatively from 150 to 250 Å; and a pore volume of from 0.5 to 1.5 mL/g, alternatively form 0.5 to 1.0 mL/g, as determined by nitrogen adsorption methods. Moreover, the hydrophobic colloidal silica comprises particles having a size and shape approximating the size and shape of the hydrophilic colloidal silica particles of component (a).

[0073] The hydrophobic partially aggregated colloidal silica of component (1) can be a single hydrophobic partially aggregated colloidal silica or a mixture comprising two or more such silicas differing in at least one property, such as surface area, pore diameter, pore volume, and hyrophobicity, particle size, and particle shape.

[0074] The concentration of component (B) in the filled silicone composition is typically from 5 to 60% (w/w), alternatively from 10 to 50% (w/w), alternatively from 20 to 40% (w/w), based on the total weight of the silicone composition. When the concentration of component (B) is less than 5% (w/w), the cured silicone product typically does not exhibit improved mechanical properties relative to the unfilled composition. When the concentration of component (B) is greater than 60% (w/w), the composition may be too viscous for certain applications. The effective amount of component (B) can be determined by routine experimentation using the methods in the Examples below.

[0075] The filled silicone composition of the present invention can comprise additional ingredients, provided the ingredient does not prevent the composition from curing to form a silicone product having superior mechanical properties. Examples of additional ingredients include, but are not limited to, hydrosilylation catalyst inhibitors, dyes, pigments, adhesion promoters, anti-oxidants, heat stabilizers, UV stabilizers, flame retardants, surfactants, flow control additives, and inorganic fillers.

[0076] The filled silicone composition of the instant invention is typically prepared by mixing components (A) and (B) and any optional ingredients in the stated proportions at ambient temperature with or without the aid of an organic solvent. Mixing can be accomplished by any of the techniques known in the art such as milling, blending, and stirring, in either a batch or continuous process. Alternatively, component (B) can be combined with the individual components of the curable silicone composition of component (A) in any order.

[0077] A cured silicone product according to the present invention comprises a reaction product of the filled silicone composition comprising components (A) and (B), described above. The filled silicone composition can be cured by exposure to ambient temperature, elevated temperature, moisture, or radiation, depending on the particular cure mechanism. For example, one-part hydrosilylation-curable silicone compositions are typically cured at an elevated temperature. Two-part hydrosilylation-curable silicone compositions are typically cured at room temperature or an elevated temperature. One-part condensation-curable silicone compositions are typically cured by exposure to atmospheric moisture at room temperature, although cure can be accelerated by application of heat and/or exposure to high humidity. Two-part condensation-curable silicone compositions are typically cured at room temperature; however, cure can be accelerated by application of heat. Peroxide-curable silicone compositions are typically cured at an elevated temperature. Epoxy-curable silicone compositions are typically cured at room temperature or an elevated temperature. Depending on the particular formulation, radiation-curable silicone compositions are typically cured by exposure to radiation, for example, ultraviolet light, gamma rays, or electron beams.

[0078] The filled silicone composition of the present invention has numerous advantages including low VOC (volatile organic compound) content and good flow. Moreover, the filled silicone composition cures to form a cured silicone product having excellent mechanical properties, such as durometer hardness, tensile strength, elongation, modulus, and tear strength, at relatively low concentrations compared with a similar silicone composition lacking the hydrophobic partially aggregated colloidal silica. The potential advantages of low filler concentrations include shorter formulation time, lower cost, and lower viscosity.

[0079] The filled silicone composition of the present invention has numerous uses including adhesives, sealants, encapsulants, and molded articles, such as o-rings.

EXAMPLES

[0080] The following examples are presented to further illustrate the coated silicone rubber article and method of the present invention, but are not to be considered as limiting the invention, which is delineated in the appended claims. Unless otherwise noted, all parts and percentages reported in the examples are by weight. The following methods and materials were employed in the examples:

[0081] Preparation of Silicone Rubber Samples

[0082] The silicone composition was compression molded using a stainless steel mold (internal dimensions: 12.7×12.7×0.16 cm), a pressure of 5000 psi (34.5 MPa), and the conditions of temperature and time specified in the Examples below.

[0083] Measurement of Tensile Strength, Elongation, and Young's Modulus

[0084] Tensile strength at rupture (MPa), ultimate elongation (%), and Young's modulus (MPa) of a silicone rubber test specimen were determined according to ASTM Standard D 412-98a using an Instron Model 5500 R Tensile Tester and dumbbell-shaped test specimens (4.5×1 cm). Young's modulus was calculated from the stress-strain curve according to ASTM Standard E 111-97. Reported values for tensile strength, elongation, and Young's modulus each represent the average of five measurements made on different silicone test specimens cut from the same silicone rubber sample.

[0085] Measurement of Tear Strength

[0086] Type B tear strength (kN/mm) of a silicone rubber test specimen was determined according to ASTM Standard D 624-00 using an Instron Model 5500R Tensile Tester. Reported values of tear strength represent the average of three measurements made on different test specimens cut from the same silicone rubber sample.

[0087] Measurement of Durometer Hardness

[0088] The durometer hardness of a silicone rubber test specimen was determined according to ASTM Standard D 2240-02 using a Conveloader Model CV-71200 Shore Type A Durometer. Three test specimens from the same silicone sample were stacked to achieve a total thickness of about 0.5 cm. Reported values for durometer hardness represent the average of three measurements performed at different locations on the same silicone rubber test specimen.

[0089] Measurement of Extrusion Rate

[0090] The extrusion rate (g/min) of a silicone composition absent the Catalyst and Inhibitor was determined according to ASTM Standard C 1183-91 using a pressure of 90 psi (0.62 MPa).

[0091] Measurement of Light Transmittance

[0092] The percent transmittance of a silcone rubber test specimen was determined using an XL-211 Hazegard Hazemeter equipped with a tungsten-halogen lamp.

[0093] Measurement of Surface Area, Pore Diameter, and Pore Volume

[0094] The surface area (m²/g) , pore diameter (Å), and pore volume (mL/g) of a hydrophobic partially aggregated colloidal silica were determined by nitrogen adsorption using a Micrometrics ASAP 2010 Analyzer.

[0095] Analysis of Hydrophobic Partially Aggregated Silica

[0096] The extent of surface treatment (% w/w) was determined by digesting samples of the treated silica in the presence of potassium hydroxide and tetraethoxysilane and then analyzing the digest by gas chromatography using a flame ionization detector and an octane internal standard to determine the concentrations of the various silane species. The amount of SiO₂ was determined by difference.

[0097] Immediately before analysis, the silica sample was dried in an oven at 150° C. for 24 h. After cooling the sample to room temperature, the silica was manually pulverized to eliminate large clumps of silica. Approximately 0.03 to 0.05 g of the treated silica and 0.03 to 0.06 g of octane (internal standard) were combined in a reaction vial. To the mixture was added 4±0.05 g of tetraethyoxysilane and a single pellet of potassium hydroxide. A microscale stir bar was placed in the reaction vial, which was sealed with a rubber septum. A 23-gauge syringe needle (3.8 cm) was inserted through the septum and brought into contact with the bottom of the vial. A 26-gauge syringe needle (0.95 cm) was inserted into the septum to act as a vent needle. Nitrogen was passed through the longer needle at a rate of about 150 mL/min until gas bubbles were no longer observed in the mixture. The vent needle was removed and the vial was pressurized to 10 psi with nitrogen. The vial was placed into an aluminum block at a temperature of 125° C. After stirring the reaction mixture for 1 h, the vial was removed from the aluminum block and then allowed to stand in air for 15 min. The vial was placed in an ice bath for about 10 min during which time the septum was removed from the vial. Dry carbon dioxide was bubbled through the reaction mixture for 3 min, during which time a precipitate formed, indicating neutralization of the base. The mixture was centrifuged at 3000 rpm for 10 min to separate the precipitate from the liquid layer. The pH of the supernatant liquid was measured with pH paper to confirm neutralization of the base (i.e., pH 6 to 8). When the pH was greater than 8, additional carbon dioxide was bubbled through the liquid to complete neutralization. The sample was transferred to a gas chromatography vial for analysis.

[0098] Gas Chromatographic analysis was carried out using an Agilent 6890 Gas Chromatograph equipped with a flame ionization detector and a DB-1 capillary column (30 m×250 μm×1 μm). The analysis was performed using a split of 50:1, an inlet temperature of 270° C., a detector temperature of 280° C., helium carrier gas at a constant flow of 1.0 mL/min, an internal standard consisting of 20,000 to 30,000 ppm of octane in tetraethoxysilane, and the following temperature profile: hold at 50° C. for 1 min, increase to 200° C. at a rate of 4° C./min, increase to 300° C. at a rate of 20° C./min, and hold at 300° C. for 10 min.

[0099] The weight percent of the triorganosiloxane and diorganosiloxane groups on the surface of the treated silica was calculated according to the following equation: ${{wt}\quad \%} = \frac{(A)\left( R_{f} \right)\left( {{Wt},{std}} \right)\left( {{Purity},{std}} \right)\left( 10^{2} \right)}{\left( {A,{std}} \right)\left( {R_{f},{std}} \right)\left( {{Wt},{samp}} \right)}$

[0100] where:

[0101] A=Area of peak for silicon-containing group, arbitrary units

[0102] Wt,std=Weight of internal standard (octane), mg

[0103] Purity,std=Purity of internal standard (octane), wt %

[0104] A,std=Area of peak for internal standard (octane), arbitrary units

[0105] R_(f),std=Response factor for internal standard (octane)

[0106] Wt,samp=Weight of sample, mg $\begin{matrix} {R_{f} = \frac{\left( {A,{std}} \right)\left( {R_{f},{std}} \right)(R)\left( {{Wt},{ref}} \right)}{(A)\left( {{Wt},{std}} \right)\left( {{Purity},{std}} \right)}} \\ {{where}:} \\ {R = \frac{M\quad W\quad \text{of~~silicon-containing~~group}}{{Mw}\quad {of}\quad {reference}\quad {material}\quad ({trimethylethoxysilane})}} \end{matrix}$

[0107] Wt. Ref=Weight of reference material (trimethylethoxysilane), mg

[0108] The following chemical substances were used in the examples:

[0109] Polymer A: a dimethylvinylsiloxy-terminated poly(dimethylsiloxane) having a viscosity of about 55 Pa.s at 25° C.

[0110] Polymer B: a dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane) having an average of 145 dimethylsilxoane units and 3 methylvinylsiloxane units per molecule, and a viscosity of 0.35 Pa.s at 25° C.

[0111] Cross-linking Agent: a trimethylsiloxy-terminated poly(dimethylsiloxane/methylhydrogen-siloxane) having an average of three dimethylsiloxane units and five methylhydrogensiloxane units per molecule and containing about 0.8% of silicon-bonded hydrogen atoms.

[0112] Inhibitor: 1-Ethynyl-1-cylcohexanol.

[0113] Catalyst: a mixture consisting of 92% of a dimethylvinylsiloxy-terminated poly(dimethylsiloxane) having a viscosity of about 0.45 Pa.s at 25° C., 7% of 1,3-divinyl-1,1,3,3-tetramethyldisiloxane, and 1% of platinum complex of 1,3-divinyltetramethyldisiloxane.

[0114] Silica Filler A: an aqueous suspension of colloidal silica sold under the trade name SNOWTEX-PS-S by Nissan Chemical Industries (Tokyo, Japan). The suspension consists of 13% (w/w) of amorphous silica (SiO₂), less than 0.2% (w/w) of Na₂O, and water. The suspension has a viscosity of 10 mPa.s at 25° C., a pH of 10.1, a specific gravity of 1.08 at 20° C., and a particle size of about 125 nm (dynamic light-scattering method).

[0115] Silica Filler B: an aqueous suspension of colloidal silica sold under the trade name SNOWTEX-PS-M by Nissan Chemical Industries (Tokyo, Japan). The suspension consists of 21% (w/w) of amorphous silica (SiO₂), less than 0.2% (w/w) of Na₂O, and water. The suspension has a viscosity of 9 mPa.s at 25° C., a pH of 9.7 a specific gravity of 1.14 at 20° C., and a particle size of about 127 nm (dynamic light-scattering method).

[0116] Silica Filler C: an aqueous suspension of colloidal silica sold under the trade name SNOWTEX-UP by Nissan Chemical Industries (Tokyo, Japan). The mixture consists of 20% (w/w) of amorphous silica (SiO₂), less than 0.35% (w/w) of Na₂O, and water. The suspension has a viscosity of 12.5 mPa.s at 25° C., a pH of about 10.4, and a specific gravity of 1.13 at 20° C.

Example 1

[0117] Concentrated hydrochloric acid (300 mL), 1 L of deionized water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 20 mL of 1,3-divinyltetramethyldisiloxane were combined in a 5-L flask equipped with a mechanical stirrer. Silica Filler A (1 L) was slowly added to the flask during a period of 30 min. The resulting suspension was stirred at 75° C. for 2 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed and the remaining hydrophobic colloidal silica was washed with 1 L of a solution of isopropanol (25 v/v %) in deionized water. The aqueous wash was removed and the washing procedure was repeated. After the second wash was removed, 2.5 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 120 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 2

[0118] A hydrophobic partially aggregated colloidal silica was prepared using the method of Example 1, except the volume of hexamethyldisiloxane was 305 mL and the volume of 1,3-divinyltetramethyldisiloxane was 30 mL. The yield of hydrophobic colloidal silica was 120 g. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 3

[0119] A hydrophobic partially aggregated colloidal silica was prepared using the method of Example 1, except the volume of 1,3-divinyltetramethyldisiloxane was 35 mL. The yield of hydrophobic colloidal silica was 120 g. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 4

[0120] A hydrophobic partially aggregated colloidal silica was prepared using the method of Example 1, except the volume of concentrated HCl was 200 mL, the volume of deionized water was 900 mL, 150 mL of chlorotrimethylsilane was used in place of hexamethyldisiloxane and 15 mL of chlorodimethylvinylsilane was used in place of 1,3-divinyltetramethyldisiloxane. The yield of hydrophobic colloidal silica was 51 g. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 5

[0121] Concentrated hydrochloric acid (200 mL), 0.9 L of deionized water, 750 mL of 2-propanol, 150 mL of chlorotrimethylsilane, 10 mL of chlorodimethylvinylsilane, 10 mL of chloromethylphenylvinylsilane, 10 mL of chlorodimethylphenylsilane, and 10 mL of chlorodiphenylmethylsilane were combined in a 5-L flask. Silica Filler A (1 L) was slowly added to the flask during a period of 30 min. The resulting suspension was stirred at 75° C. for 1 h and then at room temperature overnight. Toluene (500 mL) was added to the flask to effect separation of the hydrophobic colloidal silica from the aqueous phase. The aqueous phase was removed and the remaining suspension of hydrophobic colloidal silica was washed with 1 L of a solution of isopropanol (25 v/v %) in deionized water. The aqueous wash was removed, the flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 114 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1. The weight percent of phenyl-containing organosiloxy groups was not determined.

Example 6

[0122] Water (1 L), 750 mL of 2-propanol, and 300 mL of concentrated hydrochloric acid were combined in a 5-L flask equipped with a mechanical stirrer. Silica Filler A (1 L) was slowly to the flask during a period of 30 min. Simultaneously, a mixture of 313 mL of dichlorodimethylsilane and 30.5 mL dichloromethylvinylsilane was added slowly to the flask during the same 30-min period. The resulting suspension was stirred at 75° C. for 2 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed, 1 L of a solution of 2-propanol (33 v/v %) in deionized water was added to the flask, and the mixture was rapidly stirred for 1 min. The aqueous wash was removed and the washing procedure was repeated. After the second wash was removed, 2 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 225 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 7

[0123] A mixture consisting of 562.7 mL of water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 300 mL of concentrated hydrochloric acid was added to 1043.5 g of Silica Filler A (diluted with water to 10% w/w SiO₂) in a 5-L flask equipped with a mechanical stirrer. After stirring for one hour at 75° C., the aqueous solution was allowed to cool to room temperature. Methyl isobutyl ketone (500 mL) was added to the stirred mixture to effect separation of the hydrophobic colloidal silica from the aqueous phase, which was then removed. Methyl isobutyl ketone (100 mL) and 500 mL of a solution of 2-propanol (33% v/v) and water were added to the flask, followed by removal of the aqueous phase. The preceding step was repeated using 150 mL of methyl isobutyl ketone and 500 mL of the solution of 2-propanol and water. After the aqueous phase was removed, 1500 mL of methyl isobutyl ketone was added to the flask. The flask was fitted with a Dean-Stark trap and the suspension was distilled until the distillate was free of water. The remaining slurry was poured into a 18×25-cm Pyrex evaporating dish and the solvent was allowed to evaporate overnight. The hydrophobic colloidal silica was further dried in an air-circulating oven at 150° C. for 23 hours. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 8

[0124] Concentrated HCl (300 mL), 1 L of deionized water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 20 mL of 1,3-divinyltetramethyldisiloxane were combined in a 5-L flask. Silica Filler B (700 mL) was slowly added to the flask during a period of 50 min. The resulting suspension was stirred at 75° C. for 1 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed and the remaining hydrophobic colloidal silica was washed with 1 L of a solution of 2-propanol (25 v/v %) in deionized water. The aqueous wash was removed and the washing procedure was repeated. After the second wash was removed, 2.6 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 70 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 9

[0125] A mixture consisting of 1300 mL of concentrated hydrochloric acid, 200 mL of chlorotrimethylsilane and 10 mL of chlorodimethylvinylsilane was added to 400 mL of Silica Filler B in a 5-L flask equipped with a mechanical stirrer. The resulting suspension was stirred at 63° C. for 1 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed, 1 L of deionized water was added to the flask, and the reaction mixture was rapidly stirred for 1 min. The aqueous phase was removed and 500 mL of toluene was added to the flask. The flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The remaining toluene/xerogel slurry was poured into a 18×25-cm Pyrex evaporating dish and the solvent was allowed to evaporate overnight. The silica was further dried in an air-circulating oven at 120° C. for 10 hours. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 10

[0126] Concentrated hydrochloric acid (300 mL), 1 L of deionized water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 20 mL of 1,3-divinyltetramethyldisiloxane were combined in a 5-L flask. A mixture consisting of Silica Filler A (720 mL) and 265 mL of Silica Filler B was slowly added to the flask during a period of 30 minutes. The resulting suspension was stirred at 75° C. for 2 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed and the hydrophobic colloidal silica was washed with 1 L of a solution of 2-propanol (25 v/v %) in deionized water. The aqueous wash was removed and 2.7 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 110 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 11

[0127] Concentrated hydrochloric acid (300 mL), 1 L of deionized water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 15 mL of 1,3-divinyltetramethyldisiloxane were combined in a 5-L flask. A mixture consisting of Silica Filler A (250 mL) and 500 mL of Silica Filler B was slowly added to the flask during a period of 60 minutes. The resulting suspension was stirred at 75° C. for 2 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed and the hydrophobic colloidal silica was washed with 500 mL of a solution of 2-propanol (40 v/v %) in deionized water. The aqueous wash was removed and the washing procedure was repeated. After the second wash was removed, 2.5 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap, and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 45 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 12

[0128] Concentrated HCl (300 mL), 1 L of deionized water, 750 mL of 2-propanol, 300 mL of hexamethyldisiloxane, and 20 mL of 1,3-divinyltetramethyldisiloxane were added to a 5-L flask. Silica filler C (680 mL) was slowly added to the flask during a period of 50 min. The resulting suspension was stirred at 75° C. for 1 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed and the hydrophobic colloidal silica was washed with 1 L of a solution of 2-propanol (25 v/v %) in deionized water. The aqueous wash was removed and the washing procedure was repeated. After the second wash was removed, 2.6 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap and the suspension was distilled until the distillate was free of water. The suspension was spray-dried in a Buchi B-191 Mini Spray Drier using compressed nitrogen, an aspirator setting of 50%, a pump setting of 50%, an inlet temperature of 220° C., and an outlet temperature of 140° C., to produce 105 g of hydrophobic partially aggregated colloidal silica. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1.

Example 13

[0129] A mixture consisting of 1 L of concentrated hydrochloric acid, 100 mL of chlorotrimethylsilane, and 5 mL chlorodimethylvinylsilane was added to 250 mL of Silica Filler C. The resulting suspension was stirred at 60° C. for 1 h, during which time the hydrophobic colloidal silica separated from the aqueous phase. The aqueous phase was removed, 500 mL of deionized water was added to the flask, and the mixture was rapidly stirred for 1 min. The aqueous wash was removed, 610 mL of deionized water was added to the flask, and the mixture was rapidly stirred for 1 min. The aqueous wash was removed, 1 L of water was added to the flask, and the mixture was stirred rapidly for 1 min. The aqueous wash was removed and 1 L of toluene was added to the flask. The flask was fitted with a Dean-Stark trap and the suspension was distilled until the distillate was free of water. The remaining slurry was poured into a 18×25-cm Pyrex evaporating dish and the solvent was allowed to evaporate overnight. The treated silica was further dried in an air-circulating oven at 120° C. for 19 hours. The physical properties and composition of the hydrophobic colloidal silica are shown in Table 1. TABLE 1 Surface Area Pore Diam. Pore Vol. Analysis of Hydrophobic Silica, Wt % Example (m²/g) (Å) (mL/g) Me₃SiO_(1/2) Me₂ViSiO_(1/2) Me₂SiO MeViSiO MeSiO_(3/2) 1 132 222 1.09 4.07 0.21 0.13 0.00 0.02 2 143 144 0.52 3.68 0.54 0.33 0.00 0.02 3 158 214 1.15 4.05 0.35 0.14 0.00 0.01 4 146 250 1.2 4.14 0.34 0.28 0.00 0.02 5 142 181 1.01 4.11 0.22 0.35 0.01 0.03 6 33 274 0.19 0.01 0.00 36.78 3.94 0.18 7 178 157 0.99 4.39 0.00 0.03 0.00 0.00 8 81 283 0.69 2.62 0.14 0.10 0.00 0.01 9 96 238 0.74 3.50 0.13 0.27 0.00 0.01 10 116 252 1.03 3.51 0.19 0.08 0.00 0.01 11 102 213 0.58 3.10 0.11 0.09 0.00 0.01 12 173 101 0.72 5.49 0.27 0.12 0.00 0.01 13 198 70.7 0.59 8.31 0.29 0.28 0.00 0.00

Example 14

[0130] A silicone composition was prepared by first adding the hydrophobic colloidal silica of Example 1 to a mixture consisting of 90% of Polymer A and 10% of Polymer B in an amount sufficient to achieve a concentration of 28% (w/w), based on the weight of the final silicone composition. The silica was added to the mixture at a rate of 1 g/min in a Haake Rheocord System 90 Mixer equipped with a Rheomix 600 mixing head with sigma mixing blades operating at 50 rpm. After the addition was complete, the mixture was mixed at 60° C. for 1 h and then allowed to cool to 40° C. during a period of 20 min. Crosslinking Agent was added to the mixture in an amount sufficient to provide 1.5 silicon-bonded hydrogen atoms per vinyl group in Polymer A and Polymer B combined, to produce a silicone base. After mixing for 30 min, 0.15 mL of Inhibitor was added to the silicone base. Catalyst was then added to the mixture in sufficient amount to provide from 10 to 15 ppm of platinum metal, based on the weight of the final silicone composition. The extrusion rate of the silicone base was 61 g/min.

Examples 15a and 15b

[0131] In Example 15a, a sample of the silicone composition of Example 14 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 15b, a sample of the silicone composition of Example 14 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 2.

Example 16

[0132] A silicone composition was prepared using the method of Example 14, except the concentration of the hydrophobic colloidal silica was 30% (w/w). The extrusion rate of the silicone base was 37 g/min.

Examples 17a and 17b

[0133] In Example 17a, a sample of the silicone composition of Example 16 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 17b, a sample of the silicone composition of Example 16 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h The physical properties of the silicone rubber products are shown in Table 2.

Example 18

[0134] A silicone composition was prepared using the method of Example 14, except the concentration of the hydrophobic colloidal silica was 34% (w/w). The extrusion rate of the silicone base was 11 g/min.

Examples 19a and 19b

[0135] In Example 19a, a sample of the silicone composition of Example 18 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 19b, a sample of the silicone composition of Example 18 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 2.

Example 20

[0136] A silicone composition was prepared using the method of Example 14, except the concentration of the hydrophobic colloidal silica was 30% (w/w) and the mixture of Polymer A, Polymer B, and hydrophobic colloidal silica was mixed at room temperature for 1 h instead of 60° C. for 1 h, immediately before addition of the Cross-linking Agent. The extrusion rate of the silicone base was 46 g/min.

Examples 21a and 21b

[0137] In Example 21a, a sample of the silicone composition of Example 20 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 21b, a sample of the silicone composition of Example 20 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° for 1 h. The physical properties of the silicone rubber products are shown in Table 2. TABLE 2 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 15a 42 5.18 437 0.71 1.33 2.25 40.63 85 15b 47 5.99 499 1.17 1.90 2.94 — 79 17a 41 6.22 702 0.68 1.34 2.19 47.63 86 17b 47 6.31 537 1.14 1.91 2.98 — 78 19a 46 7.82 715 1.15 1.92 2.94 43.61 85 19b 52 8.27 605 1.49 2.40 3.56 — 83 21a 47 5.29 421 1.06 1.87 3.07 43.43 83 21b 48 5.75 407 1.18 2.05 3.36 — 82

Example 22

[0138] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 28% (w/w) of the hydrophobic colloidal silica of Example 2. The extrusion rate of the silicone base was 45 g/min.

Examples 23a and 23b

[0139] In Example 23a, a sample of the silicone composition of Example 22 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 23b, a sample of the silicone composition of Example 22 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 3.

Example 24

[0140] A silicone composition was prepared using the method of Example 22, except the concentration of the hydrophobic colloidal silica was 28% (w/w). The extrusion rate of the silicone base was 23 g/min.

Examples 25a and 25b

[0141] In Example 25a, a sample of the silicone composition of Example 24 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 25b, a sample of the silicone composition of Example 24 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 3.

Example 26

[0142] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 30% (w/w) of the hydrophobic colloidal silica of Example 3. The extrusion rate of the silicone base was 44 g/min.

Examples 27a and 27b

[0143] In Example 27a, a sample of the silicone composition of Example 26 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 27b, a sample of the silicone composition of Example 26 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 3.

Example 28

[0144] A silicone composition was prepared using the method of Example 26, except the concentration of the hydrophobic colloidal silica was 28% (w/w). The extrusion rate of the silicone base was 77 g/min.

Examples 29a and 29b

[0145] In Example 29a, a sample of the silicone composition of Example 28 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 29b, a sample of the silicone composition of Example 28 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 3. TABLE 3 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 23a 48 5.13 406 1.09 1.79 2.88 — 83 23b 50 4.95 365 1.22 1.98 3.14 33.27 79 25a 47 4.27 389 1.30 1.84 2.68 — 83 25b 50 4.94 374 1.40 2.20 3.21 34.68 82 27a 45 4.96 463 0.92 1.72 2.81 41.51 82 27b 51 5.25 364 1.37 2.18 3.38 — 82 29a 41 4.61 453 0.85 1.43 2.35 36.08 82 29b 48 5.30 408 1.12 1.85 2.99 — 81

Example 30

[0146] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 30% (w/w) of the hydrophobic colloidal silica of Example 4. The extrusion rate of the silicone base was 52 g/min.

Examples 31a and 31b

[0147] In Example 3 la, a sample of the silicone composition of Example 30 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 31b, a sample of the silicone composition of Example 30 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 4.

Example 32

[0148] A silicone composition was prepared using the method of Example 30, except the concentration of the hydrophobic colloidal silica was 34% (w/w). The extrusion rate of the silicone base was 20 g/min.

Examples 33a and 33b

[0149] In Example 33a, a sample of the silicone composition of Example 32 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 33b, a sample of the silicone composition of Example 32 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 4.

Example 34

[0150] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 34% (w/w) of the hydrophobic colloidal silica of Example 5. The extrusion rate of the silicone base was 59 g/min.

Examples 35a and 35b

[0151] In Example 35a, a sample of the silicone composition of Example 34 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 35b, a sample of the silicone composition of Example 34 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 4. TABLE 4 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 31a 42 5.20 530 0.94 1.51 2.39 36.60 82 31b 48 5.78 460 1.24 1.92 2.99 — 79 33a 50 6.27 509 1.32 2.07 3.14 38.53 81 33b 53 6.45 455 1.63 2.45 3.63 — 75 35a 49 6.12 500 1.10 1.91 3.14 39.58 79 35b 49 6.57 527 1.32 2.08 3.28 — 78

Example 36

[0152] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 30% (w/w) of the hydrophobic colloidal silica of Example 6. The extrusion rate of the silicone base was 110 g/min.

Examples 37a and 37b

[0153] In Example 37a, a sample of the silicone composition of Example 36 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 37b, a sample of the silicone composition of Example 36 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 5.

Example 38

[0154] A silicone composition was prepared using the method of Example 36, except the concentration of the hydrophobic colloidal silica was 38% (w/w). The extrusion rate of the silicone base was 44 g/min.

Examples 39a and 39b

[0155] In Example 39a, a sample of the silicone composition of Example 38 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 39b, a sample of the silicone composition of Example 38 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 5.

Example 40

[0156] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 25% (w/w) of the hydrophobic colloidal silica of Example 7 and the mixture of Polymer A, Polymer B, and hydrophobic colloidal silica was mixed at room temperature for 1 h instead of 60° C. for 1 h, immediately before addition of the Cross-linking Agent.

Examples 41a and 41b

[0157] In Example 41a, a sample of the silicone composition of Example 40 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 41b, a sample of the silicone composition of Example 40 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 5. TABLE 5 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 37a 16 0.32 82 0.28 — — — 70 37b 19 0.37 75 0.38 — — 0.88 73 39a 36 1.01 64 0.88 — — — 69 39b 42 1.26 59 1.10 — — 1.93 67 41a 40 4.27 481 0.74 1.25 2.11 — 86 41b 42 4.60 421 0.92 1.54 2.57 — 86

Example 42

[0158] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 34% (w/w) of the hydrophobic colloidal silica of Example 8. The extrusion rate of the silicone base was 84 g/min.

Examples 43a and 43b

[0159] In Example 43a, a sample of the silicone composition of Example 42 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 43b, a sample of the silicone composition of Example 42 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 6.

Example 44

[0160] A silicone composition was prepared using the method of Example 42, except the concentration of the hydrophobic colloidal silica was 38% (w/w). The extrusion rate of the silicone base was 40 g/min.

Examples 45a and 45b

[0161] In Example 45a, a sample of the silicone composition of Example 44 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 45b, a sample of the silicone composition of Example 44 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 6.

Example 46

[0162] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 34% (w/w) of the hydrophobic colloidal silica of Example 9.

Examples 47a and 47b

[0163] In Example 47a, a sample of the silicone composition of Example 46 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 47b, a sample of the silicone composition of Example 46 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 6.

Example 48

[0164] A silicone composition was prepared using the method of Example 46, except the mixture of Polymer A, Polymer B, and hydrophobic colloidal silica was mixed at room temperature for 1 h instead of 60° C. for 1 h, immediately before addition of the Cross-linking Agent.

Examples 49a and 49b

[0165] In Example 49a, a sample of the silicone composition of Example 48 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 49b, a sample of the silicone composition of Example 48 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 6.

Example 50

[0166] A silicone composition was prepared using the method of Example 46, except the concentration of the hydrophobic colloidal silica was 43% (w/w). A sample of the silicone composition was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. The physical properties of the silicone rubber product are shown in Table 6. TABLE 6 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 43a 41 5.67 651 0.77 1.23 2.01 36.08 78 43b 43 6.54 574 0.95 1.51 2.48 — 72 45a 45 6.93 659 1.00 1.62 2.58 41.15 78 45b 51 7.03 563 1.25 1.92 2.99 — 73 47a 47 6.01 586 0.91 1.41 2.39 — 79 47b 50 5.03 408 1.05 1.64 2.79 — 78 49a 52 5.94 457 1.12 1.77 3.01 — 80 49b 54 6.11 409 1.19 1.92 3.35 — 79 50 53 8.47 612 1.44 2.24 3.53 — 81

Example 51

[0167] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 30% (w/w) of the hydrophobic colloidal silica of Example 10. The extrusion rate of the silicone base was 68 g/min.

Examples 52a and 52b

[0168] In Example 52a, a sample of the silicone composition of Example 51 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 52b, a sample of the silicone composition of Example 51 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 7.

Example 53

[0169] A silicone composition was prepared using the method of Example 51, except the concentration of the hydrophobic colloidal silica was 34% (w/w). The extrusion rate of the silicone base was 26 g/min.

Examples 54a and 54b

[0170] In Example 54a, a sample of the silicone composition of Example 53 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 54b, a sample of the silicone composition of Example 53 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 7.

Example 55

[0171] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 25% (w/w) of the hydrophobic colloidal silica of Example 11. The extrusion rate of the silicone base was 150 g/min.

Examples 56a and 56b

[0172] In Example 56a, a sample of the silicone composition of Example 55 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 56b, a sample of the silicone composition of Example 55 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 7.

Example 57

[0173] A silicone composition was prepared using the method of Example 55, except the concentration of the hydrophobic colloidal silica was 34% (w/w). The extrusion rate of the silicone base was 60 g/min.

Examples 58a and 58b

[0174] In Example 58a, a sample of the silicone composition of Example 57 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 58b, a sample of the silicone composition of Example 57 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 7. TABLE 7 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 52a 42 6.16 567 0.88 1.52 2.55 42.03 82 52b 45 5.52 441 1.10 1.83 2.99 — 76 54a 49 6.65 530 1.06 1.99 3.25 40.28 81 54b 51 6.79 467 1.48 2.38 3.66 — 80 56a 38 4.33 440 0.60 1.09 2.00 — — 56b 39 4.81 438 0.57 1.12 2.14 23.64 78 58a 39 6.27 670 0.79 1.35 2.21 — 81 58b 43 6.39 545 1.05 1.76 2.83 41.15 80

Example 59

[0175] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 30% (w/w) of the hydrophobic colloidal silica of Example 12. The extrusion rate of the silicone base was 163 g/min.

Examples 60a and 60b

[0176] In Example 60a, a sample of the silicone composition of Example 59 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 60b, a sample of the silicone composition of Example 59 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 8.

Example 61

[0177] A silicone composition was prepared using the method of Example 59, except the concentration of the hydrophobic colloidal silica was 34%(w/w). The extrusion rate of the silicone base was 105 g/min.

Examples 62a and 62b

[0178] In Example 62a, a sample of the silicone composition of Example 61 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 62b, a sample of the silicone composition of Example 61 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 8.

Example 63

[0179] A silicone composition was prepared using the method of Example 59, except the concentration of the hydrophobic colloidal silica was 38% (w/w). The extrusion rate of the silicone base was 56 g/min.

Examples 64a and 64b

[0180] In Example 64a, a sample of the silicone composition of Example 63 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 64b, a sample of the silicone composition of Example 63 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 8.

Example 65

[0181] A silicone composition was prepared using the method of Example 14, except the hydrophobic colloidal silica of Example 1 was replaced with 39% (w/w) of the hydrophobic colloidal silica of Example 13.

Examples 66a and 66b

[0182] In Example 66a, a sample of the silicone composition of Example 65 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min and 150° C. for 10 min. In Example 66b, a sample of the silicone composition of Example 65 was compression molded under a continuous pressure of 34.5 MPa at room temperature for 3 to 5 min, 150° C. for 10 min, and 200° C. for 1 h. The physical properties of the silicone rubber products are shown in Table 8. TABLE 8 Young's Modulus Durometer Tensile (MPa) Tear Light Hardness Strength Elongation at Elongation = Strength Trans. Example (Shore A) (MPa) (%) 50% 100% 200% (N/mm) (%) 60a 37 2.75 285 0.85 1.42 2.30 15.24 86 60b 42 3.14 248 1.25 1.90 2.90 — 79 62a 38 3.00 321 0.86 1.51 2.39 14.54 89 62b 44 3.68 329 1.17 1.92 2.91 — 82 64a 44 2.80 247 1.23 1.88 2.66 — 85 64b 48 2.65 190 1.14 1.99 2.92 14.89 87 66a 53 4.78 405 1.30 2.17 — — 87 66b 56 4.62 350 1.41 2.34 — — 85

[0183] Replace Paragraph [0005] with the following Paragraph.

[0184] U.S. Pat. No. 6,051,672 to Burns et al. discloses a silicone rubber composition comprising hydrophobic non-aggregated colloidal silica prepared by a method comprising reacting an aqueous suspension of a hydrophilic non-aggregated colloidal silica having an average particle diameter greater than about 4 nm with a silicon compound selected from the group consisting of organosilanes and organosiloxanes at a pH less than about pH 4 in the presence of a sufficient quantity of a water-miscible organic solvent to facilitate contact of the hydrophilic non-aggregated colloidal silica with the silicon compound at a temperature within a range of about 20 C to 25 C for a time period sufficient to form a hydrophobic non-aggregated colloidal silica.

[0185] Replace Paragraph [0068] with the following Paragraph.

[0186] Additionally, before removing the water-immiscible organic solvent, the non-aqueous phase can be distilled to remove water. The distillation can be carried out at atmospheric or subatmospheric pressure at a temperature that depends on the boiling point of the water-immiscible organic solvent. The distillation is typically continued until the distillate is free of water. The distillation is typically continued until the distillate is free of water. 

That which is claimed is:
 1. A filled silicone composition, comprising: (A) a curable silicone composition; and (B) 5 to 60% (w/w) of a hydrophobic partially aggregated colloidal silica.
 2. The filled silicone composition according to claim 1, wherein the curable silicone composition is selected from a hydrosilylation-curable silicone composition, a peroxide curable silicone composition, a condensation-curable silicone composition, an epoxy-curable silicone composition, an ultraviolet radiation-curable silicone composition, and a high energy radiation-curable silicone composition.
 3. The filled silicone composition according to claim 2, wherein the curable silicone composition is a hydrosilylation-curable silicone composition comprising (i) an organopolysiloxane containing an average of at least two silicon-bonded alkenyl groups per molecule, (ii) an organohydrogensiloxane containing an average of at least two silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure the composition, and (iii) a hydrosilylation catalyst.
 4. The filled silicone composition according to claim 1, wherein the hydrophobic partially aggregated colloidal silica is prepared by a method comprising reacting (1) a silica sol comprising at least one hydrophilic partially aggregated colloidal silica with (2) an organosilicon compound selected from (a) at least one organosilane having the formula R¹ _(a)H_(b)SiX_(4-a-b), (b) at least one organocyclosiloxane having the formula (R¹ ₂SiO)_(m), (c) at least one organosiloxane having the formula R¹ ₃SiO(R¹SiO)_(n)SiR¹ ₃, and (d) a mixture comprising at least two of (a) (b), and (c), in the presence of (3) water (4) an effective amount of a water-miscible organic solvent, and (5) an acid catalyst, to produce the hydrophobic partially aggregated colloidal silica and an aqueous phase, wherein R¹ is hydrocarbyl or substituted hydrocarbyl; X is a hydrolysable group; a is 0, 1, 2, or 3; b is 0 or 1; a+b=1, 2, or 3, provided when b=1,a+b=2 or 3; m has an average value of from 3 to 10; and n has an average value of from 0 to
 10. 5. The filled silicone composition according to claim 4, wherein component (1) is a moniliform silica sol.
 6. The filled silicone composition according to claim 4, wherein component (1) is an elongated-shaped silica sol.
 7. The filled silicone composition according to claim 4, wherein X is selected from —Cl, Br, —OR³, —OCH₂CH₂OR³, CH₃C(═O)O—, Et(Me)C═N—O—, CH₃C(═O)N(CH₃)—, and —ONH₂, wherein R³ is C₁ to C₈ hydrocarbyl or halogen-substituted hydrocarbyl.
 8. The filled silicone composition according to claim 4, wherein m has an average value of from 3 to
 5. 9. The filled silicone composition according to claim 4, wherein n has an average value of from 0 to
 4. 10. The filled silicone composition according to claim 4, wherein component (4) is a monohydric alcohol.
 11. The filled silicone composition according to claim 4, wherein the concentration of the hydrophilic partially aggregated colloidal silica of component (1) is from 1 to 20% (w/w).
 12. The filled silicone composition according to claim 4, wherein the mole ratio of component (2) to the SiO₂ in component (1) is from 0.1 to
 5. 13. The filled silicone composition according to claim 4, wherein the concentration of component (4) is from 5 to 35% (w/w).
 14. The filled silicone composition according to claim 4, wherein the hydrophobic partially aggregated colloidal silica precipitates from the aqueous phase.
 15. The filled silicone composition according to claim 14, further comprising separating the hydrophobic partially aggregated colloidal silica from the aqueous phase.
 16. The filled silicone composition according to claim 15, further comprising washing the hydrophobic partially aggregated colloidal silica with water.
 17. The filled silicone composition according to claim 16, further comprising suspending the hydrophobic partially aggregated colloidal silica in a water-immiscible organic solvent.
 18. The filled silicone composition according to claim 17, further comprising removing the water-immiscible organic solvent by evaporating or spray drying.
 19. The filled silicone composition according to claim 18, further comprising before removing the water-immiscible organic solvent, distilling the suspension of the hydrophobic partially aggregated colloidal silica to remove water.
 20. The filled silicone composition according to claim 4, wherein the hydrophobic partially aggregated colloidal silica remains suspended in the aqueous phase.
 21. The filled silicone composition according to claim 20, further comprising treating the aqueous suspension with a water-immiscible organic solvent in an amount sufficient to form a non-aqueous phase comprising the water-immiscible organic solvent and the hydrophobic partially aggregated colloidal silica.
 22. The filled silicone composition according to claim 21, further comprising separating the non-aqueous phase from the aqueous phase.
 23. The filled silicone composition according to claim 22, further comprising washing the non-aqueous phase with water.
 24. The filled silicone composition according to claim 23, further comprising removing the water-immiscible organic solvent by evaporating or spray drying.
 25. The filled silicone composition according to claim 24, further comprising before removing the water-immiscible organic solvent, distilling the non-aqueous phase to remove water.
 26. The filled silicone composition according to claim 1, wherein the concentration of component (B) is from 10 to 50% (w/w).
 27. The filled silicone composition according to claim 26, wherein the concentration of component (B) is from 20 to 40% (w/w).
 28. A cured silicone product comprising a reaction product of the filled silicone composition according to claim
 1. 29. A cured silicone product comprising a reaction product of the filled silicone composition according to claim
 3. 30. A cured silicone product comprising a reaction product of the filled silicone composition according to claim
 4. 